Spectrum® 3D PLA Matt Filament 1.75mm 1kg Spool

Spectrum PLA Matt Filament

Spectrum's matte filaments are based on PLA and are chemically modified to give the matte finish after printing. In addition, the PLA Matt Filaments are more temperature resistant, less brittle and have UV protection. The appealing aesthetics and excellent properties make the Spectrum PLA Matt Filaments an absolute eye-catcher and indispensable for anyone who likes to create 3D models.

Well-known material in matt look

The polylactic acid used is also the basis of the Spectrum PLA Matt filaments. As a result, you can rely on the high printing efficiency, easy processing and high tensile strength. However, thanks to chemical modification and the use of additives, the PLA Matt material is improved even further. Here, for example, the brittleness is reduced, the temperature resistance and the impact bending strength are increased and, in addition, UV stabilization is achieved. Despite all these improvements, the PLA Matt material remains biodegradable and thus for the most part environmentally friendly.

A wide range of applications thanks to a special look

Thanks to the matte surface, Spectrum 3D PLA Matt filaments offer you a wide range of possible applications. You can create decorative objects that are very robust and resistant and exude an elegant look. Thanks to the modified composition, the visibility of the individual layers on the side surfaces of the manufactured elements is significantly minimized. Thus, with PLA Matt filaments, you can create and present high-quality architectural models in addition to decorative items.

Fields of application:

• Interior design and decoration
• architectural models
• educational objects
• Initial production of industrial designs to visualize concepts.

Technical data:

• Brand: Spectrum
• Material: PLA (Polylactic Acid)
• Wire thickness: 1,75 mm
• Dimensional accuracy: + / - 0.03 mm
• Content / Weight: 1kg
• Length: ca. 335,45 m
• Recommended print temperature: 190 - 230 °C
• Recommended print bed temperature: 0 - 45 °C
• Suggested printing speed: 40 - 110 mm/s
• Material density: 1.24 g/cm3
• Melt flow index (MFR): 6 g / 10 min

• Impact strength unnotched at +23°C: 14 kJ/m2
• Impact strength not notched at +23°C: 3.5 kJ/m2
• Tensile elongation: 2.9 %
• Tensile strength: 30 MPa
• Heat forming temperature: 66 °C - 116 °C
• Glass transition temperature: 85 °C
• modulus of elasticity: 2750 MPa
• Active fan: Yes
• Layer height: 0.05 - 0.30 mm
• Shell thickness: 0.40 – 2.70 mm
• Closed construction space: not necessary
• Drying box: not necessary
• Ruby or hardened nozzle: not necessary

• Spool diameter: 200mm
• Spool width: 68mm
• Spool hub hole diameter: 52mm
• Spool gross weight: ca. 1247g
• Weight of an empty Spool: ca. 247g