Spectrum® 3D PLA SILK Filament 1.75mm 1kg Spool

Spectrum PLA Silk Filament

Do you want to increase the quality and variety of your prints and are still looking for a filament that is suitable for this? Then just try it with the Spectrum PLA Silk filaments. These filaments combine all the positive properties, of pure PLA, and combine them with high-quality color concentrates for a unique silky matte surface. The user-friendly material is suitable for all 3D printers and is easy and clean to process. 

PLA material with silk matte structure

The Spectrum PLA Silk Filament is manufactured on the basis of pure polylactic acid, which, through the use of color concentrates, obtains the effect of a silky matte surface structure. The classic properties of PLA, i.e. simplicity and printing efficiency with very low shrinkage and relatively high tensile strength, are maintained. Use Spectrum PLA Silk filaments when you value simplicity in printing and want to produce aesthetically pleasing models.

High aesthetics with satin sheen

Thanks to the satin surface texture, the manufactured models, the visibility of individual layers on the lateral surface is significantly reduced. Thus, you create unique models, which you can wonderfully set in scene as decoration. The models with the satin sheen are also popular in interior design.

Fields of application:

• decorative art
• interior design
• educational projects
• advertising material
• Initial production and demonstration of designed finished and semi-finished products

Technical data:

• Brand: Spectrum
• Material: PLA (Polylactic Acid)
• Wire thickness: 1,75 mm
• Dimensional accuracy: + / - 0.03 mm
• Content / Weight: 1kg
• Length: ca. 340,95 m
• Recommended print temperature: 210 - 240 °C
• Recommended print bed temperature: 40-60 °C
• Suggested printing speed: 40 - 110 mm/s
• Material density: 1.23 g/cm3
• Melt flow index (MFR): 6 g /10 min

• Impact strength not notched at +23°C: 6 J/m
• Tensile elongation: 0,05
• Tensile strength: 45 MPa
• Tensile modulus: 2700 MPa
• Flexural strength: 72 MPa
• Heat forming temperature: 50 °C
• Glass transition temperature: 57 °C
• Active fan: Yes
• Layer height: 0.05 - 0.30 mm
• Shell thickness: 0.40 – 2.70 mm
• Closed construction space: not necessary
• Drying box: not necessary
• Ruby or hardened nozzle: not necessary

• Spool diameter: 200mm
• Spool width: 68mm
• Spool hub hole diameter: 52mm
• Spool gross weight: ca. 1247g
• Weight of an empty Spool: ca. 247g